Aluminum Ingot 99.7%

???Product Presentation???  
Products Name:Pure Aluminum Ingot99.9%
Chemical Composition: Al
Weight: 20/25kg
Al (Min): 99%-99.9%
Place of Origin: China (Mainland)
Appearance: silvery white
Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. 
Products meet the nationalstandard GB/T1196-2002. The surface of ingot is clean and smooth.
Packaging: 25Kg /Ingot, Packed in wooden case, Net weight 1000Kg/ Case,or as customer''s requirements.  
    
???Specification ??? 
The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00, and
below.
 
Grade                                                    Chemical Composition   %
                    Al≥                                               impurities ≤
                                      Si      Fe      Cu            Ga        Mg        Zn       Mn    others       Sum
Al99.9        99.90    0.50   0.07    0.005      0.02      0.01      0.025    -      0.010         0.10
Al99.85      99.85    0.80   0.12    0.005      0.03       0.02      0.030    -      0.015         0.15
Al99.7        99.70    0.10   0.20   0.010      0.03       0.02      0.030    -      0.030         0.30
Al99.6        99.60    0.16    0.25   0.010      0.03       0.03      0.030    -      0.030          0.40
Al99.5        99.50    0.22    0.30   0.020      0.03       0.05      0.050    -      0.030         0.50
Al99.00      99.00    0.42   0.50    0.020      0.03        0.05     0.050     -     0.050         1.00

???Usage???   
1. Mainly used for melting ingot 
2. Discontinuous melting with scrap
3. Easy control and operation
4. Fast melting
5. Used for industry such as automobile,pinning and weaving,electron broadly and so on.